Effect of Plasma Treatment on Titanium Surface on the Tissue Surrounding Implant Material

Both, the in vitro and the in vivo analysis show an altered titanium surface, resulting in a better wettability and thus an increased amount of new bone formation in the tissue surrounding the implant.

Authors: Tsujita, H.; Nishizaki, H.; Miyake, A.; Takao, S. & Komasa, S.

Publication: Effect of Plasma Treatment on Titanium Surface on the Tissue Surrounding Implant Material, International Journal of Molecular Sciences, 2021, 22.

First published: https://www.mdpi.com/1422-0067/22/13/6931

Total recap:

The effect of surface modification of titanium implants on bone formation is the object of several investigations. Especially cold atmospheric plasma treatment shows promising results. While most investigations focus on in vitro investigations, this work from Tsujita et al. links the surface characterization with investigations of hard tissue integration in vivo.

Titan implants were treated with cold atmospheric plasma generated by the piezobrush® PZ2 for 30 seconds at a distance of 10 mm. The process gas was generated by the device from the ambient air.

The surface properties were investigated by SEM, XPS and contact angle analysis. The SEM analysis revealed that the plasma treatment did not change the surface structure. The effect of the plasma is based on surface manipulation in atomic scale, which results in a reduced carbon load on the surface, as shown with XPS. The water contact angle was before the treatment 32°, after the plasma treatment the implant was superhydrophilic.

The tissue integration of implants is strongly dependent on the cell adhesion behavior. Therefore, the adhesion of RBMC cells was investigated. While the cells on the untreated titanium (Fig. 2 b,d) have an oval shape, the cells on the treated titanium (Fig. 2 a,c) are enlarged and filamentous pseudopodia were acquired.

Additional to the in vitro experiments, plasma-treated and untreated titanium implants were implanted in the rat femur. After eight weeks of healing, the implant was further investigated. In figure 3, you see a three-dimensional computer tomography picture of the implant. It is clearly obvious that the amount of new bone formation is for the treated implant higher (Fig. 3 a) than for the untreated implant (Fig. 3 b).

From quantitative histomorphometric analysis (fig. 4), both, the bone area ratio (BA), and the bone-to-implant contact (BIC) could be determined. Both values are strongly enhanced for the plasma treated implants. In combination with the histopathological image of the bone tissue around the implant and the fluorescent labelled dynamic tissue morphometry, a early enhanced osseointegration and formation of hard tissue could be confirmed.

Early osseointegration is important to achieve initial stability after implant placement. In the investigation, control and experimental groups included untreated screws and those irradiated with atmospheric-pressure plasma using the piezobrush, respectively. The femurs of rats were used for in vivo experiments. Micro-CT analysis showed that more new bone was formed in the test group than in the control group. Similar results were shown in histological analysis. Thus, titanium screw, treated with atmospheric-pressure plasma, could induce high hard tissue differentiation even at the in vivo level.

Read the whole report here.